Casting superalloy is widely used in aviation engine, aerospace engine, gas turbine, ship, metallurgy, petroleum and glass industry for it's super anti-heat, anti-oxidation and anti-corrosion property.
DTL's directionally solidified alloy and single crystal alloy improve the components' operating temperature and thus prolonged the durability and reliability of the components enormously.
All kinds of alloy developed by HEXIN can match the property of the alloy developed and produced in the advanced countries or even better.
Typical nickel based master alloy ingots' grades like: K418(IN713),K4169,GH4099,K4648,K424,IN738,GH4169,GH3536,GH3625,M247,etc.,
Diameter: 250~8100mm , length: 120~700mm
| Classification | Grade | Tensile Properties | Creep-rupture Properties | Range of Application | ||||
| Temp, ℃ | Yield Strength, Mpa | Tensile Strength, Mpa | Elongation, % | Temp / Stress | Creep Rupture Life, h | |||
| For conventional equiaxed crystal casting | k417 | 900 | 640 | 745 | 10 | 900℃/200MPa | >1000 | Suitable for up to 950°C. High alloy strength, good plasticity and low density. |
| K418 | 900 | 455 | 670 | 9.5 | 900℃/127MPa | >6000 | Suitable for up to 900°C. High creep strength and oxidation resistance. | |
| K465 | 900 | 695 | 790 | 10 | 900℃/209MPa | >2000 | Suitable for up to 1050°C. High strength at high temperatures and corrosion resistance. | |
| For directional solidification casting | DZ22 | 980 | 480 | 652 | 21 | 980℃/186MPa | >210 | Suitable for up to 1050°C. Good medium and high temperature performance and resistance to cold and heat fatigue. |
| DZ408 (CM247LC) | 980 | 460 | 660 | 28 | 980℃/186MPa | >250 | Suitable for up to 1050°C. Good creep resistance, fatigue resistance and high temperature bearing capacity. | |
| For single crystal casting | CMSX-4 | 980 | 570 | 700 | 18 | 1100℃/137MPa | >100 | Suitable for up to 1100°C. High strength at high temperatures, good overall performance, stable structure. |
| Rene N5 | 980 | 615 | 857 | 23 | 1100°C/137MPa | >120 | Suitable for up to 1100°C. High strength at high temperatures, good overall performance, stable structure. | |
| KZ4 | 980 | 623 | 752 | 26 | 1100°C/137MPa | >100 | Suitable for up to 1100°C. Good overall performance, stable organization, low density and high cost performance. | |
| For single crystal castingIII | KZ30 | 980 | 640 | 860 | 35 | 1100C/137MPa | >260 | Suitable for up to 1150°C. Excellent high temperature performance, good structure stability. |
Casting superalloy is widely used in aviation engine, aerospace engine, gas turbine, ship, metallurgy, petroleum and glass industry for it's super anti-heat, anti-oxidation and anti-corrosion property.
DTL's directionally solidified alloy and single crystal alloy improve the components' operating temperature and thus prolonged the durability and reliability of the components enormously.
All kinds of alloy developed by HEXIN can match the property of the alloy developed and produced in the advanced countries or even better.
Typical nickel based master alloy ingots' grades like: K418(IN713),K4169,GH4099,K4648,K424,IN738,GH4169,GH3536,GH3625,M247,etc.,
Diameter: 250~8100mm , length: 120~700mm
| Classification | Grade | Tensile Properties | Creep-rupture Properties | Range of Application | ||||
| Temp, ℃ | Yield Strength, Mpa | Tensile Strength, Mpa | Elongation, % | Temp / Stress | Creep Rupture Life, h | |||
| For conventional equiaxed crystal casting | k417 | 900 | 640 | 745 | 10 | 900℃/200MPa | >1000 | Suitable for up to 950°C. High alloy strength, good plasticity and low density. |
| K418 | 900 | 455 | 670 | 9.5 | 900℃/127MPa | >6000 | Suitable for up to 900°C. High creep strength and oxidation resistance. | |
| K465 | 900 | 695 | 790 | 10 | 900℃/209MPa | >2000 | Suitable for up to 1050°C. High strength at high temperatures and corrosion resistance. | |
| For directional solidification casting | DZ22 | 980 | 480 | 652 | 21 | 980℃/186MPa | >210 | Suitable for up to 1050°C. Good medium and high temperature performance and resistance to cold and heat fatigue. |
| DZ408 (CM247LC) | 980 | 460 | 660 | 28 | 980℃/186MPa | >250 | Suitable for up to 1050°C. Good creep resistance, fatigue resistance and high temperature bearing capacity. | |
| For single crystal casting | CMSX-4 | 980 | 570 | 700 | 18 | 1100℃/137MPa | >100 | Suitable for up to 1100°C. High strength at high temperatures, good overall performance, stable structure. |
| Rene N5 | 980 | 615 | 857 | 23 | 1100°C/137MPa | >120 | Suitable for up to 1100°C. High strength at high temperatures, good overall performance, stable structure. | |
| KZ4 | 980 | 623 | 752 | 26 | 1100°C/137MPa | >100 | Suitable for up to 1100°C. Good overall performance, stable organization, low density and high cost performance. | |
| For single crystal castingIII | KZ30 | 980 | 640 | 860 | 35 | 1100C/137MPa | >260 | Suitable for up to 1150°C. Excellent high temperature performance, good structure stability. |